Good Vibrations: Ultrasonic Acoustically Assisted Inline Drying for Waterborne Wood Coatings

By Anthony Carignano, business development and strategic marketing specialist

PCT Engineered Systems, LLC

SUBMITTED

Non-profiled plywood was used in the testing of USA drying in wood conversion applications.


SUBMITTED

Gabe Moore, Technology Scout, Tarkett North America, was part of the team involved in proving USA drying can be used for waterborne wood coating applications.


SUBMITTED

TABLE 1. Heraeus Fusion F450 Radiometry Used for Testing


SUBMITTED

TABLE 2. Ultrasonic Acoustically Dried UV-WB Wood Coating Test Data


SUBMITTED

FIGURE 1. Gloss Measurement Angles


SUBMITTED

TABLE 3. Ultrasonic Acoustically Dried UV-WB Wood Coating Test Data (Drying Process vs. Substrate Type vs. Gloss Measurement vs. Adhesion)


SUBMITTED

TABLE 4. One Hour and 24 Hour Stain Test Results for Acoustically Dried and Energy Cured Substrates Containing UV-Cured Aliphatic Polyurethane Dispersion


SUBMITTED

Stain tests were performed with birch and white oak test panels.

Click Thumbnails to View

“Acoustic waves are characterized by their frequency (cycles per second), wavelength (distance between cycles) and amplitude (height of the wave). Depending on the frequency of the waveform, sound waves can be classified as infrasonic, sonic and ultrasonic. Sonic waves have frequencies between 20 and 20,000 Hz, which correspond to the frequency range of human hearing. Waves with frequencies below 20 Hz are classified as infrasonic, while waves with frequencies above 20,000 Hz are classified as ultrasonic.”1

The use of ultrasonic acoustic waves and their effect on the drying and film performance of industrial inline coatings is supported by a broad and growing body of research. During the past decade, commercial acceptance of ultrasonic acoustically assisted (USA) heat and mass transfer drying has grown rapidly in consumer product inline converting applications, such as printing and adhesive lamination. USA drying provides energy cost savings, increased throughput and reduced footprint. It also has proven to be a unique fit for niche applications, such as cold seal adhesives, in which drying completeness is critical for tack. Although USA drying has been successfully evaluated as an alternative energy-efficient drying method for certain high free moisture content wood species, the white space between waterborne coatings, wood substrates and USA drying remains uncharted.

According to a recent multi-client market study on the global radiation-cured products industry: “The market for energy curable waterborne applications will grow globally by 14% on an annualized basis through 2017. Wood-coating applications currently represent 85% of energy-curable waterborne volumes, followed by vinyl composite tile.”2 Motivated by environmental concerns and increasingly stringent regulations, many wood conversion companies are shifting away from organic solvent, high VOC-based coatings where possible. Coatings that contain organic solvents are a major source of man-made volatile organic compounds (VOCs). “Volatile organic chemicals have a high vapor pressure and a lower boiling point than water at room temperature, allowing them to easily become vapors or gases in air.”3 Adopting waterborne (WB) energy-curable coatings is a preferred way of mitigating VOCs. Waterborne energy curing gives an appearance similar to solvent-based coatings, eliminates the plastic look of 100% solid ultraviolet- (UV) or electron beam- (EB)cured coatings and provides superior solvent and impact resistance. In addition, clear WB energy-cured coatings are known to show off more woodgrain than 100% solid-based systems. Although advancements in microwave drying have made WB energy curing more attractive to end users, the need to thermally dry sensitive substrates still remains a limiting factor in the proliferation of WB UV/EB energy curing in wood conversion applications. “Heat is a particular challenge for resinous/oily woods, such as pine, fir, spruce and mahogany. When resinous woods become too hot, the resins or pitch come to the surface or ‘bleed,’ causing problems with coating adhesion and discoloration.”4

As an alternative to drying waterborne wood-coating systems with conventional direct heat methods, this article discusses USA-assisted indirect airborne drying. Lower energy consumption, reduction in total residual solvents, increased output and smaller production footprints are all direct benefits of using ultrasonic acoustic drying technology for inline wood coating applications, in addition to the ability to dry heat-sensitive substrates at near ambient room temperature. In addition, ultrasonic acoustic drying technology is versatile and compatible with water- and organic-solvent hybrid solvent systems. As legislation relating to carbon emissions, energy consumption and chemicals of concern becomes more stringent, near room temperature drying that also has the ability to act as a gateway to more effectively using hybrid waterborne coatings systems will continue to become more of a preferred capital investment option for a variety of inline coating applications.

Breaking boundary layers and bubbles

Although USA drying has been evaluated and adopted as an alternative energy-efficient drying method for many consumer product packaging kraft paper and filmic plastic applications, a significantly uncharted opportunity remains for the adoption of USA drying in wood conversion applications, where advancements in industrial drying technology have been slowly evolving for some time.

To prove that USA drying can be used for waterborne wood coating conversion applications just as easily as it is used in the world of printing and packaging, Heat Technologies, Inc. (HTI) conducted a series of tests at its commercial pilot facility at Georgia Power’s Industrial Resource Center in Atlanta, Georgia. All drying tests completed used commercially available industrial-scale USA drying and ancillary equipment resources available through the resource center.

During all test work, the USA drying equipment was set at 40 kHz of acoustically charged air at temperatures at or below 120°F.5, 6 All wet films during testing were dried in less than one minute simulating a five-foot longitudinal array of acoustic slots that generate ultrasonic oscillating waves created with pneumatic air and electricity. Conversely, a typical conventional drying oven used for the same conversion application would be more than 15 feet in length and fed with natural gas. “The drying process for energy-curable and conventional waterborne polyurethane dispersions in the wood conversion market (in North America) also would normally consist of three minutes of laminar air at 104°F (40°C) followed by three minutes of hot air impingement drying at 122°F (50°C), cured then with an integrated UV mercury vapor lamp.”7 When doubled, the total drying time would be at least 10 minutes! The same drying process is applied to base coats and sealer topcoats.

All wood substrates used during the testing were non-profiled plywood. The substrates were sanded with a 200 grit sandpaper prior to and post application of sealer coats, followed by energy curing of base and top coats. All panels used were 254x254x5mm and horizontally dried while conveyed under an acoustic field at 15 to 30 feet per minute. The ambient conditions during testing were measured at a relative humidity of 69% with a room temperature from 76°F to 86°F. Relative humidity conditions below 20% during finishing applications are known to exacerbate micro-foaming (bubbling) in waterborne spray applications. Although USA drying at certain levels of intensity is known to have a de-foaming effect on liquids, this phenomenon was not evaluated at lower ambient humidity levels during testing. However, research gathered for testing at HTI supports that ultrasonic processing does provide “de-bubbling and leveling benefit to wet coating films”8, with specific reference made to “polymer coating applications using ultrasonic drying.”9

Many wood coating formulators stated their concern about the near room temperatures and very short drying times associated with USA drying during testing. Most said that during shorter drying periods, highly profiled shapes (e.g. recessed cabinet doors) have a tendency to trap water, which creates potential for white streaks. Neither profiled nor recessed shapes were addressed as a part of this test work. However, given the ability to customize the shape, oscillating reach and air velocities of the acoustic drying equipment used for this test work, the 3D shapes and profiles typically found within kitchen cabinetry, door and molding conversion applications should not be an obstacle for this drying method. The body and depth of research available on the usage of ultrasound relating to the dehydration of 3D porous objects10 also supports this claim.

Beyond the 3D shapes and profiles typically found within wood conversion applications, drying waterborne coating systems can be challenging in any environment because of the extended resonance time required – and especially when either low solids conditions, such as with stains, or when higher wet mil thickness film systems are applied. HTI President Gene Plavnik has commented: “In many cases, the formation of an air boundary on the surface of the coating film inhibits wet film drying and promotes skinning. It’s the boundary layer of air sitting on top of the wet surface of the film, in effect, that acts like an invisible shield that does not allow air to penetrate into the surface of the wet film in order to begin its evaporation process. Although increased heat and air will accelerate the evaporation of the film, there are diminishing returns in the rate of drying once skinning occurs.”11

Desirably, the top surface of the wet film is not dried in a way that causes premature skinning prior to drying the full thickness of the film. Adding oscillating pressure to the wet film in the form of ultrasonic waves entrained with heat provides greater moisture defusing efficiency, thus providing disruption of the boundary layer. The oscillating pressure wave effect of USA drying does not stop at the boundary level. Pressure waves generated by acoustic drying “propagate into coating wet films and substrates, creating microchannels and generating localized displacement of water molecules and air bubbles as well. At increased intensities of acoustically charged air, these waves have a heat-generating and cavitation effect on water molecules and entrained air bubbles,”12 which results in quicker drying and better leveling of the film.

Regardless of coating backbone chemistry, waterborne coatings applied at high speed often contain air bubbles (i.e., foaming) and will foam to some degree during mixing and application. Air bubbling and foaming often occur for a variety of mechanical shear, chemical and substrate reasons. Additives, such as surfactants and de-foamers, are used frequently to de-bubble/de-foam coatings and provide good surface leveling and gloss. Without effectively addressing de-foaming when air bubbles dry and collapse, the resulting small, round concave depressions (i.e. cratering) that are left behind create visible surface defects that detract from gloss. Lower substrate gloss levels dampen light reflectance. Higher gloss coatings tend to enrich and brighten substrate color.

Waterborne wood coating USA drying test work completed

During recent drying performance testing at Georgia Power’s Industrial Resource Center, the basic characteristics of several acoustically dried and energy-cured clear coat aliphatic polyurethane dispersions (PUD) were evaluated. Although energy-curable WB PUDs from several suppliers were evaluated, one specific UV-PUD – Ucecoat® 7788 – was chosen based on its known usage for industrial wood coating applications and overall water release performance. Ucecoat 7788 contains 40% total solids and has a pH of 7.5-8.5. 3% Irgacure® 500 from BASF was used as the photoinitiator with the chosen PUD at 3% total formulation weight. Although Dow Acrysol® RM 8W was used to provide body and thickening to the UV-PUD, no de-foamers or leveling agents were used to modify film characteristics. Dried film samples were sent to two testing facilities for independent gloss and crosshatch adhesion analysis. All samples were cured using a Heraeus Noblelight Fusion UV F450 120 W/cm (300 W/inch) H-bulb UV-curing system available on site with the radiometry conditions shown in Table 1. Table 2 shows time to dry and UV cure test data.

Discussion regarding ultrasonic acoustically dried UV-WB coating test data and results

In Table 2, acoustic air temperatures used for drying were from 105°F and 120°F (40.5°C to 49°C). All wood panels and Leneta 1A charts dried with acoustic assistance reached maximum surface temperatures of 90°F to 100°F range (32.2°C to 37.7°C) under continuously charged acoustic air flows. A #35 Mayer rod was used to coat all Leneta 1A test charts. A 40 psi Husky gravity feed HVLP spray gun model #H4840GHVSG was used for all wood panel spray work. Three to six wet mil thicknesses were successfully applied and dried to Leneta 1A, white oak and birch panels at line speeds of 30 feet per minute. All Mayer rod control samples were dried in a Vulcan hot air convection oven at 150°F for 10 minutes. In line runs 13 through 20, both birch and white oak panels were successfully dried at a room temperature within less than one minute at line speeds of up to 30 feet per minute. In line runs 25 through 27, the addition of minimal acoustically charged heat at less than 120°F (48.9°C) reduced the pre-UV curing drying time to less than 30 seconds.

Measuring the gloss of USA dried wood coatings

Measuring gloss consists of shin­ing a beam of light onto a surface of a coated substrate at a fixed angle, followed by determining the percentage of light reflected at exactly the opposite angle. Perfectly smooth coated surfaces should reflect everything at the angle of incidence and should have a gloss value of 100. Conversely, a coated surface with roughness or other imperfections, such as craters, will cause a percentage of the light beam to scatter, reducing the amount of light that is recap­tured – therefore reducing the gloss value (Figure 1). Gloss angle refers to the angle (relative to the vertical) at which the light beam strikes the surface. “The most common gloss angles are 20, 60 and 85 degrees.”13

In Table 3, Leneta charts, along with birch and white oak panel, were selected for gloss measurement by a nationally recognized wood coatings research laboratory. The aliphatic PUD system described previously was applied to both 1A Leneta charts with a #35 Mayer rod. Charts were dried at 150°F in a Vulcan hot air convection oven for 10 minutes and used the testing company’s acoustic field at room temperature in approximately 15 seconds at 40 kHz.

Also shown in Table 3, birch panel sample #16 was spray-applied with a four mil wet sealer and a four mil wet top coat and then dried with 40 kHz of acoustically charged air at a line speed of 15 feet per minute. White oak panel sample #26 was spray-applied with a three mil base and top coats to one side of the panel. The panel then was dried with 40 kHz of acoustically charged air at a line speed of 30 feet per minute. Sealer and top coats were cured for all substrates using the radiometry provided in Table 1, with gloss measurements provided in Table 3.

The basic gloss measurement work in Table 3 suggests that gloss performance is not negatively affected by ultrasonic acoustic drying. In fact, USA drying may have helped build gloss, via the rupturing and micro-leveling of trapped bubbles through sonification of the wet coating film as a byproduct of the ultrasonic acoustic drying process.

Gloss measurement and observations made by the manufacturer of Leneta charts for both coated 1A Leneta charts and wood panels suggest that acoustically assisted drying provides better leveling during drying. The supplier of Leneta charts commented: “The oven-dried Leneta charts clearly show striations from the wire-wound applicator (#35 Mayer rod), while striations were harder to find on the acoustically dried charts.” Furthermore, the supplier said: “Measurements with a 60° gloss meter indicated less gloss variation across the acoustically dried chart.” Indeed, several research reports located prior to the completion of testing validated the effects of ultrasound in de-bubbling. In fact, the effects of using ultrasonic oscillating waves to de-bubble coating systems has been used for well over a decade within the consumer product printing and conversion industry. “Ultrasonics help in de-bubbling, as the standing waves that form drive the bubbles to the nodes of the sound waves, where they coalesce to form larger bubbles, which then rise faster to the surface. Ultrasonics also help in de-gassing, as the ultrasonic energy acts to nucleate bubbles, reducing the supersaturation of any dissolved air.”14

Free moisture loss of wood panels during ultrasonic acoustic drying

There were concerns at the testing company and among wood coating chemists consulted for this project regarding the usage of USA drying for waterborne wood-coating applications and its effect on substrate free moisture loss before and during performance testing. The use of high-power ultrasound as a method of drying freshly milled wood is documented, and there are several references to significantly shortening the drying times of freshly cut timber with minimal heat.

Research reports reviewed during the writing of this article suggest that “water diffusivity during the ultrasonic acoustic drying process is due to cavitation and the creation of microscopic channels in the intercellular tissue of wood.”15 Regarding concern that any resonance time under an ultrasonic acoustic field might damage or negatively affect dried film performance: The free moisture content on several wood substrates was measured before and after acoustic drying and UV curing. At point of sale, white oak panels used for testing ranged from 7.4% to 8.6% in free moisture content. After 26 seconds of resonance time at 40 kHz, the free moisture content of substrates coated with eight wet mils of UV waterborne polyurethane dispersion sealer and top coat dropped by 1.7% (from 7.4% to 5.7%) at a consistent air temperature of 120°F (48.8°C) and maximum substrate surface temperature of 100°F (37.7°C). During a second test, after 20 seconds of resonance time at 40 kHz, overall free moisture dropped 0.2% from 8.6% to 8.4% with the same consistent air flow and substrate temperatures. The key takeaway from the free moisture testing is that, with an exposure of less than one minute, ultrasonic acoustic drying at 40 kHz with air temperatures at or less than 120°F (48.8°C) did not appear to have a negative effect on porous wood substrates, such as white oak or birch. In fact, documented scientific research on the topic suggests that the dehydration effects of USA at 40 kHz require well over 30 minutes of continuous exposure to achieve significant free moisture loss results.

Table 4 shows that birch test panel #14 and white oak test panel #27 were selected for stain testing. This chart also shows the conditions under which test panels were dried and cured. French’s® mustard, cherry Kool-Aid® concentrate and betadine stains were used. After one hour, substances were removed with a lightly moistened paper towel. A very slight mustard stain watermark remained on the white oak but faded completely after two weeks. After 24 hours, pronounced Kool-Aid, mustard and betadine stains remained visible on coated white oak substrate. The birch substrate exhibited a light watermark of mustard stain. No stain resistance differences were noted after the same stains were applied to white oak and birch panels dried with convection heating and UV cured.

Conclusions

Ultrasonic acoustically assisted drying has gained growing interest and commercial adoption from several obvious and a few novel applications during the past decade. In the European Union, the packaging conversion industry has expressed the most interest in this drying method, largely due to its energy cost savings and carbon footprint mitigation. Although inexpensive energy costs in North America may not be a compelling justification to bank on USA-assisted drying, the method’s ability to boost and maximize existing production line outputs while using minimal to no additional footprint is gaining notoriety and a few early adopters.

For wood converters seeking overall performance improvements and compliance with emerging regulatory requirements, there are learnings from the established usage of USA drying in packaging converting applications, which make the USA leap to sealers and topcoats for wood a logical next step.

This article reports promising initial results on the effects of USA-assisted drying for waterborne coating systems for wood and serves as a starting point for further evaluations in other heat-sensitive substrate applications. The improvements in film gloss, leveling and substrate adhesion revealed in this report have yet to be fully understood, vetted or scrutinized based on performance versus cost benefit. In addition, a number of finishing atmospheric and profile conditions have yet to be evaluated. Therefore, the intention of this article and associated follow-up research is to increase interest, awareness and collaboration within the inline waterborne wood coatings value chain for the adoption of USA-assisted drying as a multifunctional energy-saving option and enabler for waterborne energy-curing technology.

References

Carson, Ph.D., T.; Morris, L.; and Folkman, D. (2014). Innovative Waterborne UV Polyurethane Dispersions for Wood Coatings. RadTech Report, 28(2), 22-28.

Gutoff, E. (2005, May 4). Fundamentals of Drying Coatings. Proceedings of Tech XXVIII Technical Seminar. Lecture conducted from Pressure Sensitive Tape Council, Baltimore.

He, Z.; Fei, Y.; Peng, Y.; and Yi, S. (2013). Ultrasound-Assisted Vacuum Drying of Wood: Effects on Drying Time and Product Quality. BioResources, 8(1), 855-863. doi:10.15376/biores.8.1.855-863

Suslick, K. (1989, February 1). The Chemical Effects of Ultrasound. Scientific American, 80-86.

Valentino, G.; Leija, L.; Riera, E.; Rodriguez, G.; and Gallego, J. (2002, September 22). Wood Drying by Using High Power Ultrasound and Infrared Radiation. Retrieved November 30, 2014, from http://www.researchgate.net/publication/39397836_Wood_drying_by_using_high_power_ultrasound_and_infrared_radiation

(Endnotes)

  1. Kiyoi, E. (2014). Wood Coating with UV-LED Curing: A Focus on Heat. RadTech Report, (Issue 2), 29-34.
  2. Martini, S. (2013). Chapter 2: An Overview of Ultrasound. In Sonocrystallization of Fats. New York, NY: Springer.
  3. Kusumgar, M., Nerlfi, S., Growney, M. (2013). The Global Radiation-Cured Products Industry 2012-2017 – A Multi-Client Study. www.kusumgar-nerlfi-growney.com
  4. Volatile organic compound. (2014, November 28). In Wikipedia, The Free Encyclopedia. Retrieved 01:16, Dec. 14, 2014, from http://en.wikipedia.org/w/index.php?title=Volatile_organic_compound&oldid=635725717
  5. Kiyoi, E. (2014). Wood Coating with UV-LED Curing: A Focus on Heat. RadTech Report, (Issue 2), 29-34.
  6. A Spectra HE Ultra acoustic drying system manufactured by Heat Technologies, Inc. and located at Georgia Power’s Customer Resource Center in Dunwoody, GA, was used to complete all supporting drying data for this article.
  7. At these settings the Spectra HE Ultra consumes less than 10 kilowatts per hour of electricity.
  8. Conversation with Jim Bohannon, Senior Applications Chemist at Alberdingk Boley, Inc.
  9. Gallego-Juarez, J. (2010). High-Power ultrasonic processing: Recent developments and prospective advances. Physics Procedia, 3(1), 35-47.
  10. Barbieri, M. (Ed.). (2007, December 2). Acceleration of Textile Processes by Ultrasound Technology. Retrieved November 9, 2014, from http://cordis.europa.eu/documents/documentlibrary/127030241EN6.pdf
  11. Mohapatra, D.; and Mishra, S. (2011). CURRENT TRENDS IN DRYING AND DEHYDRATION OF FOODS. In Food Engineering (pp. 311-352). Nova Science.
  12. Plavnik, G. (2011, January 1). How acoustically-enhanced drying improves productivity, cuts energy consumption. Converting Quarterly, 63-65.
  13. Legay, M.; Gondrexon, N.; Le Person, S.; Boldo, P.; and Bontemps, A. (2011). Enhancement of Heat Transfer by Ultrasound: Review and Recent Advances. International Journal of Chemical Engineering, 2011 (Article ID 670108), 1-17.
  14. Evaluation of Weathering Effects: Visual Inspections and Instrumental Measurements. (2011, January 1). Retrieved Nov. 9, 2014, from http://www.q-lab.com/documents/public/92986a7e-2676-4a45-be6c-081624fbcb9e.pdf
  15. Gutoff, E. (2004, November 30). Eliminate Pesky Bubbles. Retrieved November 30, 2014, from http://www.pffc-online.com/technical-reports/2891-paper-eliminate-pesky-bubbles
  16. He, Zhengbin; Zhao, Zijian; Yang, Fei; and Yi, Songlin. Effect of ultrasound pretreatment on wood prior to vacuum drying. Maderas, Cienc. tecnol. (online) 2014, vol.16, n.4, pp. 395-402. Epub 21-Aug-2014. ISSN 0718-221X.

Acknowledgements

Gene Plavnik, Heat Technologies, Inc.
Ronald Obie, Wood Coatings Research Institute
Joe Peters, Leneta Company, Inc.
Gabe Moore, Tandus-Centiva
Warren Daniel, Stahl USA, Inc.
Brian Otte and Bertram Raabe, Heraeus Noblelight Fusion UV Inc.
Wayne Pettyjohn, Georgia Power CRC

Anthony Carignano is business development and strategic marketing specialist at PCT Engineered Systems, LLC. With more than 20 years of experience developing and growing new markets and applications in the specialty chemicals industry, his recent accomplishments include leading PCT’s efforts to establish a fully operational ebeam laboratory unit, which is being used for instructional and technical proof of concept purposes at Georgia Power’s Industrial Customer Resource Center in Dunwoody, Georgia. He also played an instrumental role in establishing RadTech’s inaugural hands-on UV/EB Surface Curing Workshop. Carignano is an active member of RadTech International North America and other coating and ink-related trade organizations. He has spoken globally on issues ranging from chemicals of concern to bio-renewable building block chemistries for consumer product packaging applications. Contact Anthony Carignano at awcarignano@teampct.com.