Most Recent Developments in UV-Curable Soft-Touch Coatings
By Xavier Drujon, Lisa Spagnola and Gunter Moeller
Table 1. Evaluation of “soft-touch” plate sample 19 (hard=1 soft=5).
Figure 1. Adhesion forces measured through AFM nanoindentation correlate very well with touch perception.
Figure 2. Variation of MEK rub resistance and soft-touch properties with double-bond concentration in a homogeneous series of aliphatic urethane acrylates.
Table 2. Design of Experiment – formulation.
Figure 3. Properties of selected DOE samples – first series.
Table 3. Properties of selected DOE samples – second series.
Soft-touch coatings are unique finishes that deliver the feel and appearance of a velvet or flocked fabric substrate. Tactile surface feel is one of the most sought-after features in plastics decoration. Thousands of neural receptors in our fingertips process touch differences as small as 1/300th of an inch. Touch cant be turned off, and fingertip appeal plays an influential role in buying behavior. This is particularly the case for soft-touch coatings.
This was illustrated1 in a recent paper that demonstrated “… there is evidence that integration of soft-touch coatings increases FMOT (First Moment Of Truth) and SMOT (Second Moment Of Truth) particularly in beauty and cosmetics” packaging as “customers are willing to pay a 5% price increase for packaging with soft-touch tactile coating as opposed to packaging with no tactile coatings.”
The interest shown by brand owners in tactile surface feel encompasses all B to C markets, including packaging, consumer electronics, automotive, small appliances and aerospace. Beyond just adding a feeling of quality, brands can connect with consumers through touch, using emotional engagement and visceral reaction to manipulate the connection between perception and reality.
Conventional soft-touch coatings can provide excellent soft-touch properties. They are two-part isocyanate-based chemistries in either solvent or water that use a difunctional polyol with a trifunctional hardener (isocyanate). A large portion of the formulations used are solvent-borne, with limited pot life and a requirement for an extended cure time.
There is a clear interest in a UV-curable system that can replace current 2K soft-touch coating technology. In addition, there is a need for increased resistance to mars, abrasions, stains and chemicals compared to the conventional systems.
Quantitative assessment of soft-touch coatings
Quantitative assessment of soft-touch performance of a coating remains elusive. Various authors have reported a strong influence of parameters, such as participants age2, sex3 or fingertip moisture level4, on tactile perception, just to name a few.
In our studies, experimental soft-touch plate samples were evaluated by a panel of 11 people selected among our R&D and headquarters staff. They were selected to create a range of background, age and gender. The perception of touch is complex, and ways to describe the full tactile experience quantitatively are lacking. To start, we explored only one dimension, using the attribute “hard” (1) versus “soft” (5). Table 1 reports the results obtained for “sample 19.”
We confirmed that perception of feel varies from person to person: What feels “hard” to one person might feel “soft” to another, and observers need to be trained to rate soft feel properly. We found that that using three test samples described as “rubbery,” “silky” and “velvety” as a reference helped us to establish a comprehensive “language” for our panel of volunteers.
When touching a surface, humans perceive its topography and softness by sliding a fingertip, with a certain velocity and pressure. The sensation of pleasantness or unpleasantness results, in part, from the frictional force and by the surface topography. We applied atomic force microscopy (AFM) to measure mechanical properties of coating surfaces with the goal of correlating results with touch feel.
We found that the adhesion forces measured through AFM nanoindentation correlate very well with touch perception. Average adhesion forces for two samples with a “silky” feel were highest and approximately 10 times higher than for the two “rubbery” samples. Adhesion forces of the “velvety” samples were approximately two to three times higher than those for the rubbery samples (Figure 1). While we currently do not understand the changes in the measured adhesion forces, our results, nevertheless, may be a first step in predicting touch feel based on physical properties measurements.
All AFM indentation measurements were performed with an MFP-3D atomic force microscope (AFM) from Oxford Instruments (formerly Asylum Research). HAS 60 AFM probes from Team Nanotec® with a spring constant of approximately 27 N/m and an end-radius of approximately 60 nm was used for indenting the coatings. The spring constant was determined using the Sader method5. The probes were calibrated based on force distance curves acquired on a silicon sample.
Nanoindentation of the coatings was performed in adhesive oscillatory contact. Force amplitudes of 100 nN or 200 nN were used for the oscillatory loading measurements. The frequency was 1 Hz. Data points were acquired for 60 seconds for each curve. Six to 10 curves without obvious artifacts were acquired for each sample. Custom software written in IGOR® was used for data analysis to determine elastic and storage moduli and adhesion forces. A Poisson ratio of 0.4 was assumed to calculate shear storage and loss moduli from the AFM data. The data analysis is based on the adhesive contact model put forward by Daniel Maugis.6
Soft-touch properties and cross-linking density
To improve mar, abrasion, stain and chemical resistance, UV coating chemists usually rely first on increasing cross-linking density.
We evaluated the haptic properties and the MEK rub resistance of a homogeneous series of aliphatic urethane acrylates (MW = 3,000 g/mol) with identical soft polyol segment. Cross-linking density was varied by adjusting the end chain acrylic functionality from 2 to 6 per molecule on average (Figure 2).
The resins (46,50%) were formulated with solvents (MEK and BuAc 23,25% each), photoinitiators (Irgacure 184 2,60%), matting additives (Acemat 3300 4%) and dispersant (Disperbyk 2008 0,4%). The formula was applied on glass panel 100 µm wet, dried five minutes at 55 to 60°C and cured 4x10m/min with a Fusion Hg lamp at 120W/cm.
In first approximation, for weakly cross-linked soft materials, such as the one chosen in this study, the cross-linking density of the film after cure can be considered as proportional to the double-bond concentration before cure.
In any case, as the concentration of double bonds was increased, improvement of MEK resistance was concomitant with the disappearance of the soft-touch property. During our investigations, we observed that the same dependence held true for mar, abrasion, stain or chemical resistance in most homogeneous coating systems.
Design of Experiments (DOE)
We decided to screen blends of difunctional urethane acrylate “oligomers” with trifunctional urethane acrylate monomer “cross-linkers.” In the remainder of the text:
- Difunctional urethane acrylates will be called UA1, UA2, UA3, UA4, UA5
- Trifunctional cross-linkers will be called M1, M2, M3, M4, M5
- The ratio of difunctional to trifunctional material was screened at 90:10 and 60:40.
The resins were formulated with solvents (50:50 MEK:BuAc 125 phr), photoinitiators (PL-HMPP 5phr), matting additives (Acemat 3300 8,5 phr) and dispersant (Disperbyk 2008 0,85 phr). The formula was applied on glass panel 100 µm wet, dried 5 minutes at 55 to 60°C and cured 4x10m/min with a Fusion Hg lamp at 120W/cm (Table 2).
The properties of selected DOE samples are compared with standard 2K PUR soft-touch coating in Figure 3. Formulations containing 60% difunctional material and 40% trifunctional material had the best properties, but these formulations were more rigid and had a silky versus rubbery feel.
DMA showed “silky” samples to have a higher storage modulus (300-700 mPa vs 3-4 mPa) and two phases, one with a Tg well below room temperature (about -10 to -20°C) and a second Tg around 70 to 80°C.
Based on the first set of experiments, the Design of Experiments was extended to screen combinations of cross-linker M1 with oligomers UA4 and UA5.
The combination of UA5 60% and M1 40% provides a UV system that has good feel with increased mar, abrasion, stain and chemical resistance compared to the conventional systems.
This work demonstrates the possibility of formulating solvent-based UV systems with good feel and increased mar, abrasion, stain, and chemical resistance compared to the conventional 2K-PUR systems.
Ongoing work in our laboratories on 100% UV-curable and waterborne UV-PUD soft-touch coatings will further expand the possibilities for formulators.
Finally, the combination of UV technology with 3D decorative processes – such as screen or inkjet printing – will create new possibilities in terms of 3D tactile finishes.
- Colleen Twomey, from Cal. Poly. Univ., (RadTech USA 2015)
- The effect of age on neural processing of pleasant soft touch stimuli. A. May et al., Frontiers in Behavioral Neuroscience (2014)
- Quantitative assessment of pleasant touch. G. Essick et al., Neurosciences and Biobehavioral Reviews 34 (2010) 192-203
- Rash built model of pleasant touch through active fingerprint exploration. Klocker et al. (2012) Front Neurorobot 6: 1-9
- Sader, J.E.; Larson, I.; Mulvaney, P.; White, L.R. Rev. Sci. Inst., 1995, 66, 3789
Sader, J.E.; Chon, J.W.M.; Mulvaney, P. Rev. Sci. Inst., 1999, 70, 3967
Sader, J.E.; Encyclopedia of Surface and Colloid Science, 2002, 846-856
- Maugis, D., 2000. Contact Adhesion and Rupture of Elastic Solids. Springer series in solid state sciences (Berlin Heidelberg New York: Springer-Verlag)